2
CÁC NỘI DUNG QUAN TRỌNG CỦA CHƯƠNG 2
•PHÂN BIỆT CÁC CHỈ TIÊU CƠ HỌC VÀ VẬT LÝ, ĐẶC BIỆT ĐỐI VỚI BÊ TÔNG VÀ BTCT
•KHẢO SÁT CÁC LOẠI CHỈ TIÊU CƠ-LÝ (CỦA BT)
−CẤP ĐỘ BỀN
−CƯỜNG ĐỘ CHỊU KÉO (TIÊU CHUẨN VÀ TÍNH TOÁN)
−CƯỜNG ĐỘ CHỊU NÉN (PHỔ BIẾN HƠN) (TIÊU CHUẨN VÀ TÍNH TOÁN)
−MODULE ĐÀN HỒI BAN ĐẦU VÀ MODULE BIẾN DẠNG
−CÁC LOẠI HÊ SỐ ĐỘ TIN CẬY (≶ 1)
−TÍNH CHẤT CO NGÓT (VẬT LÝ) VÀ TỪ BIẾN (CƠ HỌC) CỦA BT
•PHÂN BIỆT CÁC LOẠI CỐT THÉP
−THƯỜNG HAY THANH (TRƠN, GỜ) VÀ CÁP ƯLT
−CHỦ YẾU LÀ CƯỜNG ĐỘ CHỊU KÉO VÀ MODULE ĐÀN HỒI (CƠ HỌC)
−TÍNH TỪ BIẾN CỦA CỐT THÉP (ẢNH HƯỞNG VẬT LÝ KHÔNG ĐÁNG KỂ)
•LỰC DÍNH CỦA BT VỚI THÉP
•SƠ ĐỒ BIẾN DẠNG CỦA BTCT (DÙNG KHI TÍNH TOÁN)
•PHÂN BIỆT SƠ BỘ TẢI TRỌNG TÁC DỤNG NGẮN HẠN VÀ DÀI HẠN
I. CÁC LƯU Ý BAN ĐẦU:
•TÍNH NĂNG CƠ LÝ CỦA RIÊNG BT, THÉP VÀ KHI BT-THÉP CÙNG LÀM VIỆC TRONG BTCT, THEO CÁC
TC CỦA CÁC NƯỚC, HIỆN GẦN NHƯ NHAU. SỐ LIỆU CHÊNH LỆCH KHI QUY ĐỔI CÙNG HỆ ĐƠN VỊ,
CÓ SAI SỐ KHÔNG ĐÁNG KỂ !
•CƠ LÀ CƠ HỌC: CÁC TÍNH CHẤT KHI CÓ NGOẠI LỰC TÁC DỤNG LÊN CẤU KIỆN, HỆ CHỊU LỰC (HCL)
•LÝ LÀ VẬT LÝ: CÁC TÍNH CHẤT KHI KHÔNG CÓ NGOẠI LỰC TÁC DỤNG (CHỈ CÓ LỰC NỘI TẠI
TRONG CẤU KIỆN XUẤT HIỆN KHI ĐÔNG CỨNG) HAY KHI CÓ NHỮNG YẾU TỐ VẬT LÝ TÁC ĐỘNG
(NHIỆT ĐỘ, CO NGÓT KHÔ…)
•CHƯƠNG NÀY VÀ MÔN NÀY CHƯA XÉT ĐẾN CÁC NỘI DUNG CHUYÊN SÂU NHƯ:
-CÁC LOẠI BT ĐẶC THÙ (CƯỜNG ĐỘ CAO, CỐT SỢI, CÓ PHỤ GIA, TRỌNG LƯỢNG NHẸ, XỐP…)
-CÁC LOẠI CỐT THÉP CƯỜNG ĐỘ RẤT CAO (DÙNG TRONG BTƯLT; NHÀ TRỌC TRỜI)
-MẪU THỬ CƯỜNG ĐỘ KHÔNG ĐÚNG THEO CHUẨN KHỐI LĂNG TRỤ (CÓ CÔNG THỨC QUY
ĐỔI)
•BT LÀ VL PHỨC HỢP, NÊN TÍNH ĐỒNG NHẤT RẤT KHÓ ĐẢM BẢO, DO ĐÓ HỆ SỐ ĐỘ TIN CẬY (AT)
CỦA BT, BTCT, CÁC TIÊU CHUẨN ĐỀU THỐNG NHẤT CHỌN GIÁ TRỊ THẤP HƠN THÉP
•TÌM HIỂU TÍNH NĂNG CƠ-LÝ ĐẶC BIỆT QUAN TRỌNG, ĐỂ NẮM VỮNG CÁC HỆ SỐ (ĐIỀU CHỈNH)
XUẤT HIỆN TRONG NHỮNG CÔNG THỨC TÍNH TOÁN Ở CÁC CHƯƠNG SAU.
•KHÔNG XÉT CÁCH TÍNH TOÁN CẤP PHỐI CỦA BT (MÔN VLXD) NHƯNG CÓ XÉT KỸ ĐẾN TUỔI BT;
ĐẶC TRƯNG BIẾN DẠNG THEO t; TÍNH BÁM DÍNH; TỈ LỆ N/X
•CÁC TIÊU CHUẨN (TC) ẢNH HƯỞNG ĐẾN TÍNH TOÁN KẾT CẤU BTCT GỒM TCVN 5574-2018 (ẢNH
HƯỞNG CỦA NGA)
EUROCODE 2 HAY EC2 (ÂU CHÂU): HỆ ĐƠN VỊ SI
ACI 318 (MỸ): CÓ 2 CÔNG THỨC CHO HỆ SI VÀ ANGLO SAXON ĐỐI VỚI CÔNG THỨC THỰC
NGHIỆM (KHÁC THỨ NGUYÊN) 3
II. CÁC TÍNH NĂNG CƠ HỌC CHỦ YẾU CỦA BT:
1. CÁC ĐỊNH NGHĨA CẦN NẮM VỮNG ĐỂ PHÂN BIỆT CHO BT
EbMÔ ĐUN ĐÀN HỒI BAN ĐẦU CỦA BT KHI NÉN VÀ KÉO (MPa)
RbCƯỜNG ĐỘ CHỊU NÉN DỌC TRỤC TÍNH TOÁN CỦA BT KHI TÍNH THEO CÁC TTGH I (MPa)
Rb,n CƯỜNG ĐỘ CHỊU NÉN DỌC TRỤC TIÊU CHUẨN CỦA BT KHI TÍNH THEO TTGH I (MPa)
Rb,ser CƯỜNG ĐỘ CHỊU NÉN DỌC TRỤC TÍNH TOÁN CỦA BT KHI TÍNH THEO CÁC TTGH II
(MPa).THƯỜNG Rb,ser= Rb,n
Rbt CƯỜNG ĐỘ CHỊU KÉO DỌC TRỤC TÍNH TOÁN CỦA BT KHI TÍNH THEO CÁC TTGH II
Rbt,n CƯỜNG ĐỘ CHỊU KÉO DỌC TRỤC KHI TÍNH TOÁN TIÊU CHUẨN CỦA BT (MPa)
Rbt,ser CƯỜNG ĐỘ CHỊU KÉO DỌC TRỤC TÍNH TOÁN CỦA BT KHI TÍNH THEO CÁC TTGH II
(MPa).THƯỜNG Rbt,ser= Rbt,n
bo BIẾN DẠNG TƯƠNG ĐỐI GIỚI HẠN CỦA BT KHI NÉN ĐỀU DỌC TRỤC
bto BIẾN DẠNG TƯƠNG ĐỐI GIỚI HẠN CỦA BT KHI KÉO ĐỀU DỌC TRỤC
b,sh BIẾN DẠNG TƯƠNG ĐỐI CO NGÓT CỦA BT (SH=SHRINKAGE)
b,cr HỆ SỐ TỪ BIẾN CỦA BT (CR=CREEP)
•VỀ CẤP ĐỘ BỀN (CẤP CƯỜNG ĐỘ) CHỊU NÉN HAY KÉO CỦA BT, B HAY Bt(GRADE OF COMPRESSIVE
OR TENSILE STRENGTH OF CONCRETE): LÀ GIÁ TRỊ ĐƯỢC KIỂM SOÁT NHỎ NHẤT CỦA CƯỜNG ĐỘ CHỊU
NÉN (HAY KÉO) TỨC THỜI, TÍNH BẰNG MEGAPASCAL (MPa), VỚI XÁC SUẤT ĐẢM BẢO KHÔNG DƯỚI 95%,
ĐƯỢC XÁC ĐỊNH TRÊN CÁC MẪU LĂNG TRỤ (HAY MẪU THỬ KÉO) CHUẨN ĐÃ ĐƯỢC CHẾ TẠO, DƯỠNG HỘ
TRONG ĐIỀU KIỆN TIÊU CHUẨN VÀ THỬ NÉN (HAY KÉO) Ở TUỔI 28 NGÀY.
•ĐIỀU KIỆN SỬ DỤNG BÌNH THƯỜNG (SERVICEABILITY): LÀ ĐIỀU KIỆN SỬ DỤNG PHÙ HỢP VỚI CÁC
ĐIỀU KIỆN ĐÃ QUY ĐỊNH TRONG CÁC TC HOẶC NHIỆM VỤ THIẾT KẾ;KHÔNG VƯỢT TẢI
•ĐỘ BỀN (RESISTANCE): LÀ KHẢ NĂNG CỦA 1CK HOẶC CỦA TIẾT DIỆN NGANG CK CHỊU ĐƯỢC CÁC TÁC
ĐỘNG MÀ KHÔNG BỊ PHÁ HOẠI, MẤT ỔN ĐỊNH
•ĐỘ BỀN LÂU (DURABILITY): LÀ KHẢ NĂNG CỦA CTXD ĐẢM BẢO ĐƯỢC CÁC TÍNH CHẤT ĐỘ BỀN, VẬT LÝ
VÀ CÁC TÍNH CHẤT KHÁC YÊU CẦU THEO THỜI GIAN. 4
2. CƯỜNG ĐỘ CỦA BT
LÀ ĐẶC TRƯNG CƠ BẢN CỦA BT, PHẢN ẢNH KHẢ NĂNG CHỊU LỰC CỦA NÓ.
CƯỜNG ĐỘ ĐƯỢC XÁC ĐỊNH BẰNG CÁCH NÉN MẪU, SIÊU ÂM; KHOAN LẤY MẪU, THỬ BẬC NẨY
2.1. CƯỜNG ĐỘ CHỊU NÉN DỌC TRỤC TIÊU CHUẨN Rb,n (fc,k) :
•TCVN 5574-18, Rb,n XÁC ĐỊNH THEO MẪU KHỐI VUÔNG 151515 CM (a)
•ACI 318 VÀ EC2, KÍ HIỆU 𝑓
𝑐
′, XÁC ĐỊNH THEO MẪU LĂNG TRỤ TRÒN 6”12”(b)
•Rb,n XÁC ĐỊNH THEO MẪU LĂNG TRỤ 151560 CM (ÍT DÙNG) (c)
•THEO EC2, ĐỂ DỄ ÁP DỤNG RỘNG RẢI KÍ HIỆU fc,k XÁC ĐỊNH ĐỊNH CẢ THEO MẪU KHỐI
VUÔNG LẪN LĂNG TRỤ TRÒN (a) VÀ (b)
THÍ DỤ C25/30: GIÁ TRỊ TRƯỚC LÀ TN THEO MÃU LĂNG TRỤ TRÒN
GIÁ TRỊ SAU LÀ TN THEO MẪU KHỐI VUÔNG (XEM PHỤ LỤC)
•MẪU KHỐI VUÔNG KHÔNG TƯƠNG THÍCH CAO VỚI SỰ LÀM VIỆC THỰC TẾ CỦA CẤU KIỆN
TRONG KẾT CẤU (HCL) BẰNG MẪU LĂNG TRỤ, DO THỰC TẾ CẤU KIỆN LUÔN CÓ ĐỘ MẢNH:
VỚI CÁC MẪU THỬ DẠNG KHÁC NHAU, GIÁ TRỊ Rb,n MẪU KHỐI VUÔNG SẼ CAO NHẤT. VỚI
CÙNG 1 LOẠI BT
•DO ĐÓ, NẾU MẪU ĐEM THỬ KHÔNG TƯƠNG THÍCH, BUỘC PHẢI CÓ NHỮNG HỆ SỐ QUY ĐỔI
ĐỂ XÁC ĐỊNH ĐỘ TƯƠNG THÍCH THEO MẪU CHUẨN, NHẤT LÀ KHI KHOAN LẤY MẪU, TÌM
CƯỜNG ĐỘ (ĐỘ BỀN)
•ACI 318, LẠI CHỈ SỬ DỤNG MẪU LĂNG TRỤ TRÒN (b); (XEM PHỤ LỤC)
•DẠNG MẪU KHÁC NHAU LÀ KHÁC BIỆT CƠ BẢN VỀ CẤP CƯỜNG ĐỘ (CẤP ĐỘ BỀN) CHỊU NÉN
CỦA BT THEO NHỮNG HỆ TC KHÁC NHAU, TUY ĐIỀU KIỆN TN LÀ NHƯ NHAU 5