In this study, Bi0.5(Na1–xKx)0.5SnO3 (BNKS) ceramics (x = 0, 0.1, 0.2, 0.3, and 0.4) were fabricated via ultrasound wave before milling. The time of ball milling decreased from 20 to 1 h. The X-ray diffraction patterns show that the BNKS has a single-phase structure.
8p
vispiderman
15-06-2023
4
2
Download
-
The (1–x)BiFe0.91(Mn0.47Ti0.53)0.09O3–xBaTiO3 (BFMT–BT) lead-free ceramics have been fabricated by using the conventional solid-state reaction method. The phase structure of BFMT−BT investigated with X-ray diffraction shows a single perovskite phase. Although 20% mol of Bi2O3 was added into the raw materials in excess, the evaporation of Bi3+ ions during calcining and sintering processes is from 20 to 30% wt. relative to other elements. The effect of BaTiO3 content on the electrical properties of BFMT−BT ceramic was investigated.