The recent advances in the study of the unique capabilities of monolayer crystals had predicted piezoelectricity in two-dimensional (2D) group IV chalcogenides which are not present in their bulk forms. In this study, the predicted piezoelectric properties of was experimentally explored through Piezoelectric Force Microscopy (PFM). Tin Sulfide (SnS), Tin Selenide (SnSe), Germanium Sulfide (GeS), were exfoliated from their bulk forms by the top down methods of liquid sonication, while and Tin Disulfide (SnS2) mechanically exfoliated by tape.

82p runthenight04 02-02-2023 9 3   Download

Traditional ceramic technology combined with a two-step sintering technique has been applied to prepare 0.96(K0.48Na0.48Li0.04)(Nb0.95Sb0.05)O3-0.04Bi0.5(Na0.82K0.18)0.5ZrO3 (KNLNS-BNKZ) piezoelectric ceramics. The experimental results show that the ceramic samples have a pure perovskite structure with the coexistence of tetragonal and rhombohedral phases.

10p nguaconbaynhay10 19-02-2021 20 3   Download

The goads of this thesis: Successfully fabricated ceramic piezoelectric samples (Ba1-xCax) TiO3 (BCT) and BZT-BCT by solid phase synthesis method. BZTBCT materials must be good quality, high piezoelectric coefficient (500-600 pC / N). Studying the relationship between morphological competition and dielectric ferroelectric properties, especially with the high piezoelectric properties of materials.

26p xacxuoc4321 09-07-2019 52 7   Download

In this work, 200-nm-thick PZT films were successfully fabricated on Nb:STO substrates by a solution process. One obtained that PZT(111) peak started to appear on the Nb:STO substrate at a low annealing temperature of 450oC. Also, scanning electron microscopy observation shows smooth and homogeneous surface of PZT films on Nb:STO substrate with no grain boundary, which evidences for epitaxial-like growth of PZT thin films. Remnant polarization of 6 µC/cm2 and leakage current of 8×10-8 A were obtained at applied voltage of 5 V.

9p truongtien_09 08-04-2018 45 1   Download