Post-annealing effect on the structural and optical properties of electrophoretically coated 2D-Layered MoSe2

The samples annealed at 150 C and 250 C showed a better optical absorption in the visible and the near infrared spectral regions with dominant characteristic peaks at 691.2 nm and 801.6 nm. Further studies assured that the EPC process yielded good quality and large area MoSe2 films with exotic structural, optical and nanomorphological characteristics that are highly suitable for functional devices.